PP-Like Functional

A tough, impact-resistant material with a modulus similar to molded unfilled
polypropylene. Exhibits excellent weathering characteristics and UV stability
making it suitable for end-use part applications.

xPP405 Black

Manifolds_4661.jpg

Specifications

Property/Test
Value
Tensile Modulus/ASTM D638
1580 MPa
Ultimate Tensile Strength/ASTM D638
42 MPa
Tensile Elongation at Break/ASTM D638
87%
Flex Modulus/ASTM D790
1180 MPa
Flex Strength/ASTM D790
50 MPa
Hardness (shore D)/ ASTM D2240
80
Notched Izod/ASTM D256
62 J/m
HDT @0.45 MPa/ASTM D648
53°C
Water Absorption/ASTM D570
1.00%

xPP405-Clear

Clear bottle_4702.jpg

Specifications

Property/Test
Value
Tensile Modulus/ASTM D638
1620 MPa
Ultimate Tensile Strength/ASTM D638
39 MPa
Tensile Elongation at Break/ASTM D638
92%
Flex Modulus/ASTM D790
1500 MPa
Flex Strength/ASTM D790
69 MPa
Hardness (shore D)/ ASTM D2240
79
Notched Izod/ASTM D256
62 J/m
HDT @0.45 MPa/ASTM D648
53°C
Water Absorption/ASTM D570
2.00%

xMED412

xMED412.jpg

Specifications

Property/Test
Value
Ultimate Tensile Strength/ASTM D638
38 MPa
Tensile Elongation at Break/ASTM D638
141%
Flex Modulus/ASTM D790
1022 MPa
Flex Strength/ASTM D790
38 MPa
Hardness (shore D)/ ASTM D2240
75
Notched Izod/ASTM D256
43 J/m
HDT @0.45 MPa/ASTM D648
40°C
Water Absorption/ASTM D570
0.36%